Theoretical analysis and experiment on Eu reduction in alumina optical materials.
Autorzy
Rok wydania
2016
Czasopismo
Numer woluminu
6
Strony
2404-2412
DOI
10.1364/OME.6.002404
Kolekcja
Język
Angielski
Typ publikacji
Artykuł
Streszczenie
Density functional theory simulation with a U correction (DFT + U) was adopted to predict the proper experimental conditions required to generate divalent europium (Eu2+) in α-Al2O3 host material consolidated via vacuum consolidation. Accordingly, samples of 0.1 at% Eu2+:α-Al2O3 were obtained by gelcasting, followed by high vacuum sintering process (<10−3 Pa). The room temperature photoluminescence excitation and emission spectra of this composition were examined and characteristic broad band positioned in the blue part of spectrum was detected under UV excitation. This luminescence decay trace had two-exponential character and the average decay time of 0.1 at% Eu2+:α-Al2O3 was 0.080ms.
Licencja otwartego dostępu
Licencja na prawach której można swobodnie kopiować, rozprowadzać, zmieniać i remiksować objęty prawem autorskim utwór (Utwór-przedmiot prawa autorskiego) pod warunkiem podania imienia i nazwiska autora utworu pierwotnego oraz źródła pochodzenia utworu.
Pełny tekst licencji: https://creativecommons.org/licenses/by/3.0/pl/legalcode
Adres publiczny
Podobne publikacje
Theoretical and experimental investigation of the Tb3+ → Eu3+ energy transfer mechanisms in cubic A3Tb0.90Eu0.10(PO4)3 (A = Sr, Ba) materials.
Carneiro Neto Albano N., Moura Renaldo T., Shyichuk Andrii, Paterlini Veronica, Piccinelli Fabio, Bettinelli Marco, Malta Oscar L.