Wydział Chemii

Justyna Zeler

Joanna Cybińska

Eugeniusz Zych

2016

RSC Advances

6

57920-57928

10.1039/C6RA09588G

Naukowa

Angielski

Artykuł

Nanocrystalline powders of LuPO₄:Eu were prepared at 230 °C by a hydrothermal method. Their post-treatment at 900, 1200 and 1350 °C induced a moderate grain growth from ∼20–50 nm up to 80–300 nm. These powders were sintered at 1700 °C and such LuPO₄:Eu materials, despite the regular Eu³⁺ emission, produced a broad-band luminescence peaking at around 425 nm at room temperature. The sintered LuPO₄:Eu materials also generated an intense thermoluminescence with the maximum around 200 °C. The photoluminescence characteristics of the broad luminescence was performed in the 20–550 K range of temperature. While the intensity of this emission did not change within 20–550 K its decay time dropped from ∼823 μs (20 K) to ∼7 μs only (550 K) with the most potent decrease between 150 and 300 K. At the same time the emission peak position moved from ∼438 nm (20 K) to ∼412 nm (550 K). These data were explained as a result of a two-level emitting center with the higher state being thermally populated at the expense of the lower level.

http://dx.doi.org/10.1039/C6RA09588G

https://www.rsc.org/