Wydział Chemii

Magdalena Wilk

Elżbieta Tomaszewicz

Miłosz Siczek

Yannick Guyot

Georges Boulon

Małgorzata Guzik

2022

Journal of Materials Chemistry C

10

10083-10098

10.1039/d2tc00604a

Naukowa

Angielski

Artykuł

Herein, the structural and spectroscopic properties of a new optical material, cubic Nd³⁺-doped mixed molybdato-tungstate with the chemical formula La₂MoWO₉, which could be employed to achieve the difficult task of fabricating transparent ceramics, were investigated. The samples in the form of micro-powders were obtained via solid-state reaction and the first translucent micro-ceramics were demonstrated. The previously studied micro-ceramics activated with Yb³⁺ ions showed the segregation phenomenon of a second phase, which was very rich in Yb³⁺ ions in the grain boundary, and thus a solution to avoid this phenomenon was sought. Currently, we are interested in the use of the Nd³⁺ dopant for two reasons, i.e., laser application and its role as a structural probe. This element has an ionic radius closer to that of La³⁺ than Yb³⁺, and thus substitutes La³⁺ better in the framework. Consequently, this was beneficial to obtain a more homogenous cubic mono-phase material, and in the next step, translucent ceramics. The fundamental analysis was conducted using complementary techniques such as XRD and TEM/SEM combined with low-temperature high-resolution spectroscopic techniques to elucidate the main features of this promising optical material. A few Nd³⁺ non-equivalent symmetry sites were observed, in accordance with the crystallographic analysis. Lastly, we also showed that the spectroscopic properties of the Nd³⁺ ion embedded in the La₂MoWO₉ host lattice were correlated with its initially missing crystal structure, which was solved based on the single crystal selected from the micro-crystalline form and presented for the first time.

http://dx.doi.org/10.1039/d2tc00604a

https://www.rsc.org/