High-entropy sesquioxide X2O3 upconversion transparent ceramics.
Autorzy
Rok wydania
2020
Czasopismo
Numer woluminu
186
Strony
19-23
DOI
10.1016/j.scriptamat.2020.04.011
Kolekcja
Język
Angielski
Typ publikacji
Artykuł
In this study, a high-entropy approach was used to design a highly transparent (81.3% in-line transmittance) sesquioxide X2O3 ceramics, in which a single-phase solid solution, with the general formula (Lu0.2Y0.395Gd0.2Yb0.2Tm0.005)2O3, was obtained after sintering under vacuum with La2O3 and ZrO2 as the sintering additives. Upconversion emission from Tm3+ ion at 485 nm was demonstrated upon the 980 nm laser emission excitation as a result of cooperative energy transfer from the Yb3+ ions. High-resolution scanning electron microscope (SEM) and Energy Dispersive X-Ray Spectroscopy (EDS) elemental mapping showed that the obtained transparent ceramics were pore-free and without segregation of different elements.
Słowa kluczowe
high-entropy, Transparent ceramics, Upconversion, sesquioxide
Adres publiczny
http://dx.doi.org/10.1016/j.scriptamat.2020.04.011
Strona internetowa wydawcy
Podobne publikacje
Specifics of Spectroscopic Features of Yb3+‐doped Lu2O3 Laser Transparent Ceramics.
Boulon Georges, Guyot Yannick, Guzik Małgorzata, Toci Guido, Pirri Angela, Patrizi Barbara, Vannini Matteo, Yoshikawa Akira, Kurosawa Shunsuke, Ikesue Akio
Photo- radio- and thermoluminescence of sintered transparent Al2O3:Eu2+ in the range 15–800 K.
Bolek Paulina, Wu Yiquan, Yang Yan, Zych Eugeniusz
The effect of Gd3+ doping on luminescence properties of (Gd, Ce): SrF2 nanopowders and transparent ceramics.
Milisavljevic Iva, Wu Yiquan, Zych Eugeniusz