Wydział Chemii

Dagmara Kulesza

Joanna Trojan-Piegza

Eugeniusz Zych

2010

Radiation Measurements

45

490-492

10.1016/j.radmeas.2009.12.008

Naukowa

Angielski

Artykuł

Lu₂O₃:Tb,Hf ceramics containing 0.1% of Tb and 0–1.5% of Hf were prepared in reducing atmosphere at 1700 °C and their thermoluminescence properties were systematically studied. For comparison Tb,Ca co-doped specimen was also fabricated and investigated. The Tb,Hf ceramics shows basically a single TL band located around 180 °C as found with heating rate of 15 °C/min. Ceramics singly doped with Tb show complex TL glow curves indicating the presence of traps of very different depths. On the other hand Tb,Ca co-doping is beneficial for the development of shallow traps with the main TL band around 70 °C. Hence, the aliovalent impurities, Ca²⁺ and Hf⁴⁺, strongly influenced the traps structure in Lu₂O₃:Tb ceramics, each of them in its own specific way. Isothermal decay of Lu₂O₃:Tb,Hf at 185 °C was recorded and its shape suggest that multiple hole trapping occurs in the Lu₂O₃:Tb,Hf ceramics. Due to the different traps depths the Lu₂O₃:Tb,Hf ceramics possess properties typical for storage phosphors, while Lu₂O₃:Tb,Ca is a persistent luminescent material rather.

Lu2O3, thermoluminescence, OSL, storage phosphor

https://doi.org/10.1016/j.radmeas.2009.12.008